- Stainless steel 304 is easier to weld than 301 due to its lower carbon content. It's also non-magnetic, which makes it ideal for applications where magnetism could be a factor in the welding process. On the other hand, stainless steel 301 has higher carbon content and is magnetic, which means that it requires more care during the welding process.
standardmachining.com › stainless-steel-304-vs-301-advantages-and-differences
People also ask
Which stainless steel is better 304 or 301?
What is the tensile strength of stainless steel 304 & 301?
Does grade 301 stainless steel withstand stress?
What is Grade 304 stainless steel?
Stainless steel 304 and 301 have impressive tensile strengths: 304 has a minimum yield strength of 185,000 psi and a minimum tensile strength of 215,000 psi. The minimum yield strength for 301 is 155,000 psi and the minimum tensile strength is 190,000 psi.
May 30, 2022 · 304 is a more durable grade of stainless steel than 301. This is because 304 has a higher chromium content, which makes it more resistant to corrosion. The chromium content in 304 is 18%, while the chromium content in 301 is only 16%.
- What Is 301 Stainless Steel?
- What Is 304 Stainless Steel?
- Difference Between 301 and 304 Stainless Steel
- Conclusion
301 stainless steel is an austenitic grade alloy that contains 17% chromium, 7% nickel, and 3% manganese. It has a high tensile strength of up to 1,500 MPa as well as excellent corrosion resistance. This grade of stainless steel is also magnetic, meaning it can be easily machined and welded. Due to its high strength-to-weight ratio, it’s often used...
304 stainless steel is also an austenitic grade alloy that contains 18% chromium and 8% nickel. It has higher levels of corrosion resistance than 301 because it contains more chromium and nickel, which act as barriers against corrosion caused by moisture or other elements in the environment. This grade of stainless steel is also non-magnetic, so it...
The main difference between these two grades lies in their tensile strength; while both have excellent corrosion resistance properties, the greater tensile strength of 301 makes it better suited for applications needing higher-strength components such as fasteners or springs. Additionally, 304 has a lower cost compared to 301 due to its higher avai...
When choosing between 301 vs 304 stainless steel for your project, there are many factors that come into play, such as cost-effectiveness and application requirements. While both types offer good corrosion resistance, they differ in terms of their tensile strengths, with 304 being weaker than 301 but still providing adequate support when needed in ...
- Bhavesh Yadav
Grade 301 stainless steel, with its higher carbon content (0.15% compared to 304’s 0.08% by weight), can better withstand mechanical force. In room temperature conditions, grade 301 stainless can take up to 120 ksi (kilopounds per square inch).
Jun 12, 2023 · Stainless steel 301 may have slightly lower yields and tensile strengths than 304, but its higher levels of chromium make it ideal for applications in which corrosion resistance is important. On the other hand, stainless steel 304 has higher strength and better formability than 301 due to its increased nickel content.
Aug 15, 2023 · Discover the differences between SUS301 and SUS304 stainless steel, including their properties, strengths, and weaknesses. Learn which one is ideal for your specific application.
Oct 17, 2022 · Tensile strength. Grade 301 stainless steel has a larger carbon content (0.15% vs 0.08% by weight) than grade 304, which makes it more resistant to mechanical stress. Temperature-neutral conditions allow grade 301 stainless steel to withstand 120 ksi (kilopounds per square inch).