Tensile Strength: 81,900 psi: Yield Strength: 36,300 psi: Elongation at Break: 55%
Strength (MPa) min. (HB) Yield Strength 0.2% Proof (MPa) Rockwell B min. Elongation (% in 50mm) min. Hardness (HR B) max. Brinell max. 316 515 205 40 95 217 316L 485 170 40 95 217 316H 515 205 40 95 217 316H also has a requirement for a grain size of ASTM No 7 or coarser.
Ultimate Tensile Strength: 82.2 ksi: Yield Tensile Strength: 36.6 ksi: Shear Modulus: 11,000 ksi: Shear Strength: 58 ksi: Fatigue Strength: 30 ksi: Hardness Rockwell | Brinell: B95 | 210: Elongation at Break Percentage: 52%: Reduction of Area: 70%: Modulus of Elasticity: 28,000 ksi: Poisson's Ratio: 0.28: Machinability Percentage: 36%: Melting ...
Greater corrosion resistance. Greater tensile strength at higher operating temperatures. Acidic resistance of solutions of nitric acid of concentration as high as 5% at 50 °C. Phosphoric acid of concentration of up to 20% at 100 °C. AISI 316 stainless steel is commonly used for equipment in the pharmaceutical industry.
Nov 8, 2018 · Grade 316 stainless steel comes with a minimum tensile stress of 515 MPa, a minimum yield stress of 205 MPa, and a minimum elongation of 40% in 50mm. At room temperature, Grade 316 stainless steel also exhibits the following set of properties: Density 99 g/cm 3. Thermal Expansion 9 mm/m/°C.
0.2% Offset Yield Strength, ksi 44 30 min. 25 min. Ultimate Tensile Strength, ksi 85 75 min. 70 min. Elongation in 2 inches, % 56 40 min. 40 min. Reduction in Area, % 69 — — Hardness, Rockwell B 81 95 max. 95 max. Typical* ASTM Type 316 Type 316L *0.375 inch plate
Sep 13, 2001 · Chemical Formula. Fe, <0.03% C, 16-18.5% Cr, 10-14% Ni, 2-3% Mo, <2% Mn, <1% Si, <0.045% P, <0.03% S. Grade 316 is the standard molybdenum-bearing grade, second in importance to 304 amongst the austenitic stainless steels. The molybdenum gives 316 better overall corrosion resistant properties than Grade 304, particularly higher resistance to ...